Orca Composites is manufactured to meet the highest quality control standards and is suitable for virtually any fiberglass application. The precise manufacturing process yields some of the most sconsistent and desirable finishes on the market today.

Orca Prepreg Resins & Adhesive

Orca Composites is pleased to offer a full range of prepreg possibilities with different resin systems and reinforcements including; carbon, glass, aramid and others. The resins can be tailored to specific liquid and cured properties to cover a full range of applications and industries. Cure temperatures range from 200˚F to 310˚F and shelf life storage requirements range from 12 mos. to 30 mos. providing temperatures do not exceed 75˚F and 0˚F, respectively.

Orca Composites offers a unique thermosetting epoxy matrix resin system featuring a one-year shelf life without refrigeration. This resin is currently used for tow/roving, unitape, fabric and braid and is available for carbon, glass, aramid and other fibers. Resin content, resin flow during cure, and tack levels can be tailored to suit your process requirements.

PREPREG PRODUCT LIST

PREPREG NO.

TYPICAL USE

Density
(g/cc)

Tg(˚F/˚C)
(from G”
DMA curve”

Tensil
Modulus
(ksi/GPa)

Tensil
Strength
(ksi/MPa)

Elongation
at Break (%)

Tg after 24-hr
Water-Boil
(˚F/˚C)

Water
Absorption
(%)

Available
Fiber Foam

1423

Rocket motor cases, large structures.

1.212

240 / 116

410 / 2.83

9.5 / 65.5

5.0

199 / 93

2.5

Tow/Roving, Unitape, Fabric, Braid

1425

Sporting goods, commercial products, pressure vessels, rocket motor cases etc., where an extra long shelf life is desired and high-temperature capabilities are not required. (270˚F - 310˚F)

1.208

255 / 124

410 / 2.83

10.0 / 68.95

5.5

169 / 76

3.9

Tow/Roving, Unitape, Fabric, Braid

1439

Commercial products (pressure vessels, cryogenics, sporting goods, etc.), where high-temperature capabilities are not required.

1.202

220 / 104

390 / 2.69

10.0 / 68.95

6.3

169 / 76*

3.9*

Tow/Roving, Unitape, Fabric, Braid

1450

Commercial products, where high temperature and good hot/wet properties are required.

1.254

376 / 191

550 / 3.79

6.0 / 41.37

1.2

267 / 131

2.9

Tow/Roving, Unitape, Fabric, Braid

1452

Sporting goods, commercial products, pressure vessels, rocket motor cases, skirts, etc., where an extra long shelf life is desired and high-temperature capabilities are not required.

1.229

270 / 132

440 / 3.03

10.7 / 73.77

4.0

169 / 76*

3.9*

Tow/Roving, Unitape, Fabric, Braid

1457

Commercial products where high temperatures and good hot/wet properties are required.

1.229

270 / 132

440 / 3.03

10.7 / 73.77

4.0

169 / 76*

3.9*

 

1460

Commercial products where moderately high temperatures and good hot/wet properties are required.

1.202

322 / 161

460 / 3.17

10.0 / 68.95

3.5

237 / 114

3.3

Tow/Roving, Unitape, Fabric, Braid

1462

Commercial products where moderately high temperatures and good hot/wet properties are required.

1.211

322 / 161*

460 / 3.17*

10.0 / 68.95*

3.5*

237 / 114*

3.3*

Tow/Roving, Unitape, Fabric, Braid

1469

High pressure SCBA tanks, rocket motor cases, sporting goods, infrastructure repair, etc., where moderately low-temperature cure is required. High translation/performance in pressure vessels when used with Toray T700SC, Toho G30-700 and Mitsubishis TRH-50 and most other carbon fibers.

1.18

242 / 117

417 / 2.83

10.9 / 68.9

5.3

152 / 67

5.1

Tow/Roving, Unitape, Fabric, Braid

1476

Rocket motor cases, sporting goods, high pressure tanks, large structures, and infrastructure repair, etc., where moderately low-temperature cure is required.

1.18

275 / 135

534 / 3.68

12.0 / 82.7

3.9

172 / 78

4.4

ow/Roving, Unitape, Fabric, Braid

TF7035

ADHESIVE
Orca Composites TF7035 is a high strength modified epoxy film adhesive with a fast cure time at 250°F (120°C). This film can be supplied with or without a synthetic fabric carrier. It is designed for high peel strengths in load bearing structures. Testing of this formulation has met the requirements set forth in specification MMM-A-132, Type 1, Class 2 and exceeded the requirements of MIL-A-25463.

Used in composite, honeycomb, metal, and other adhesion applications requiring high shear strengths and corrosion resistance.Available in weight ranges .